Squeeze casting process

Squeeze casting process presentation

1. 1 MAHARASHTRA INSTITUTE OF TECHNOLOGY , PUNE Seminar on SQUEEZE CASTING PROCESS Seminar by DIPANSHU KAWLE(308030) Guided by Prof. G.P.BORIKAR

2. Contents Introduction Squeeze casting Working Process p arameters Case study Advantages & Disadvantages Applications Conclusion References MIT Pune 2

3. SQUEEZE CASTING MIT Pune 3

4. Introduction Also known as liquid-metal forging. Near net shape process - the initial production of the item is very close to the final (net) shape, reducing the need for surface finishing. Combination of casting and forging. Squeeze casting is simple and economical, efficient in its use of raw material. The process generates the highest mechanical properties attainable in a cast product . MIT Pune 4

5. Squeeze casting process working Squeeze casting consists of entering liquid metal into a preheated, lubricated die and forging the metal while it solidifies The load is applied shortly after the metal begins to freeze and is maintained until the entire casting has solidified MIT Pune 5

6. Casting parameters Casting temperatures   depend on the alloy and the part geometry. The starting point is normally 6 to 55°C above the liquidus temperature. Tooling temperatures  ranging from 190 to 315°C are normally used Pressure levels  of 50 to 140 MPa are normally used Lubrication For aluminum, magnesium, and copper alloys, a good grade of colloidal graphite spray lubricant has proved satisfactory when sprayed on the warm dies prior to casting MIT Pune 6

7. Case Study Effects Of Squeeze Casting Process Parameters On Density Of Lm20 Alloy The experiment are carried out at different squeeze casting condition to know the effect of process parameters such as squeeze pressure,Pressure duration,,Time delay & Die temperature. Experiments were conducted by varying one parameter at a time and keeping the rest of other process parameters constant. MIT Pune 7

8. Effects of Process Parameters Effects Of Time Delay Effects Of Pressure Duration Effects Of Squeeze Pressure Effects of Pouring temperature MIT Pune 8

9. MIT Pune 9

10. Advantages Little or no machining required post casting process Low levels of porosity Good surface texture Fine micro-structures with higher strength components No waste material, 100% utilization MIT Pune 10

11. Disadvantages Costs are very high due to complex tooling No flexibility as tooling is dedicated to specific components Process needs to be accurately controlled which slows the cycle time down and increases process costs. High costs mean high production volumes are necessary to justify equipment investment MIT Pune 11

12. Applications of Squeeze Casting The squeeze casting has been commercially succeeded in manufacturing parts include an Aluminium dome , ductile Iron mortar shell, and a Steel bevel gear. Aluminium automotive wheels and pistons, and gear blanks made of brass and bronze. Compared with the HPDC, the squeeze casting process with high applied pressure is a promising solution for thick magnesium castings Other parts that have been Squeeze cast include stainless steel blades, super alloy discs, MIT Pune 12

13. Conclusion In conclusion, squeeze casting technology can greatly improve the performance of aluminum alloys and other light alloys; promote the utilization of aluminum alloys instead of steel; reduce the weight of automobile, machinery equipment and military equipment; promote energy conservation and environmental protection. Finally, squeeze casting technology can greatly lessen the impurity restriction in raw material. MIT Pune 13

14. REFERENCES Najib Souissi ,Slim Souissi , Christophe Le Niniven , Mohamed Ben Amar , Chedly Bradai and Foued Elhalouani “ Optimization of Squeeze Casting Parameters for 2017 A Wrought Al Alloy Using Taguchi Method “ Maleki , A.; Shafyei , A.; Niroumand , B. Effects of squeeze casting parameters on the microstructure of LM13 alloy. J. Mater. Process. Technol. 2009 , 209 , 3790–3797. Manjunath Patel G. C1, Robins Mathew, and Prasad Krishna, “Effects of Squeeze Casting Process Parameters on Density” Department of Mechanical Engineering, National Institute of Technology Karnataka , Elsevier, 2013 MIT Pune 14