Covestro Products for Wood Metal Coatings 02-2023.pdf

Wood coatings

1. TITLE SLIDE | LOGO 2
Covestro
Products for
Wood Coatings
January 2023

2. TEXT -LOGO
Covestro CA products for Wood Coatings
2
1K
2K
Solventborne& -free 2K PUR systems
Desmophen+ Desmodur
Waterborne 1K systems
Neocryl, NeoRez& NeoPac
Waterborne 2K PUR systems
Bayhydrol+ Bayhydur

3. PRODUCT MAP SHORT_LOGO
3
Drying Speed
Flexibility
Desmodur
®
& Desmodur
®
ultra for Parquet Lacquers, Furniture & other 2K PUR Wood Coatings
Aromatic TDI-based Polyisocyanates
L 75
L 67
ultra
IL
IL
1451
BA
Ultra
IL1351
BA
HL
E
2605/1
better light &
yellowing stability
better toluene &
NC compatibilty
more cost
effective
Easy matting
faster drying
LTDI Polyisocyanates
HLTDI/HDI Polyisocyanate
ETDI/MDI Prepolymer
ultra
L 75
LLow monomer ultra grades (<0,15)

4. TEXT -LOGO
Aromatic TDI-based Polyisocyanates
4
Desmodur
®
& Desmodur
®
ultra for Wood and other Coatings
Desmodur
®Monomer
base
Solid
content[%]
Viscosity
@23°C [mPas]
NCO content
[%] supplyform
Equivalent
weight
Functio-
nality
Gel time [h]
withD‘dur1300X
comments
L 67BA TDI 67 in BA 600 11.9 350 2.7 17 Fast dryingcrosslinkerfor
furniture, wood, concrete,
industrialmetal& protective
coatingsaswellasadhesives
L 67 MPA/XTDI 67 (MPA/X 1:1)1600 11.9 350 2.7 13
L 75 TDI 75 in EA 1600 13.3 315 2,7 9.5
ultra L 75TDI 75 in EA 1600 13.3 315 2,7 9.5 Ultra-lowmonomer grade ofL 75
HL BA HDI/TDI60 in BA 2200 10.5 400 4.4 3 Fast dryingcoatingswithhigher
elasticity& light fastnessthan
DesmodurL 75HL EA HDI/TDI60 in BA 1100 10.5 400 4.4 4
ultra IL BATDI 51 in BA 2000 8.0 525 4.5 2
Very hardand fast drying
crosslinkerforwood, furniture
and papercoatings
ultra IL EATDI 51 in EA 700 8.0 525 4.5 3.5
ultra IL 135 BATDI 51 in EA 1300 8.0 525 4.5 2.5
IL 1451 BATDI 51 in BA 250 7.4 565 4.8 3 bettercompatibiltythanIL 1351

5. TEXT -LOGO
Covestro CA products for various Coating Technologies
5
1K
2K
Solventborne& -free 2K PUR systems
Desmophen+ Desmodur
Waterborne 1K systems
Neocryl, NeoRez& NeoPac
Waterborne 2K PUR systems
Bayhydrol+ Bayhydur

6. PRODUCT MAP SHORT_LOGO
6
Solvent-based Desmophen
®
grades for 2K PUR Wood Coatings crosslinked with Desmodur
®
L/IL
Polyester Polyols
Drying Speed
OH content on solids [%]
800
1100
1700
PL
800
1300
PL
817
Parquet Lacquers Furniture Coatings
fastest drying speed
higher
gloss &
flexibility
higher
flexibility
& scratch
resistance

7. TABLE -LOGO
7
Solvent-based Desmophen
®
grades for 2K PUR Wood Coatings crosslinked with Desmodur
®
L/IL
Polyester Polyols
Desmophen
®
Type
Supply form
OH-content [%]
supplyform
Viscosity 23 °C
[mPas]
Properties
1300
Non dryingfattyacid
mod. PES
100%
75% in X
75% in BA
4.3
3.2
3.2
-
3500
1000
Forhigh solid primersand topcoats(clear&
pigmented)
PL 817
Non dryingfattyacid
mod. PES
75% in X/MEK 3.3 10000
Highlyreactive, veryuniversal forsealers&
topcoats
PL 800
Non dryingsynthetic
fattyacidmod. PES
70% in X 2.5 1500 SimilartoRD 181, lowerapplicationviscosity
800 HighlybranchedPES
100%
85% in BA
85% in MPA
8.6
7.3
7.3
-
11000
11000
Forhardandchemicalresistantair-drying2K
systemswithhigh impactandabrasionresistance
1100 BranchedPES 100% 6.5
400
(70% in MPA)
Combinationresinforhighlybranched
Desmophentypes
1700 Linear PES 100% 1.3 17500
Flexibilizingresinto improvetoughness, durability
and abrasionresistance

8. TEXT -LOGO
Covestro CA products for various Coating Technologies
8
1K
2K
Solventborne& -free 2K PUR systems
Desmophen+ Desmodur
Waterborne 1K systems
Neocryl, NeoRez& NeoPac
Waterborne 2K PUR systems
Bayhydrol+ Bayhydur

9. TEXT -LOGO
Covestro CA products for various Coating Technologies
9
1K
2K
Solventborne& -free 2K PUR systems
Desmophen+ Desmodur
Waterborne 1K systems
Neocryl, NeoRez& NeoPac
Waterborne 2K PUR systems
Bayhydrol+ Bayhydur

10. PRODUCT MAP SHORT_LOGO
10
Drying speed
Blocking resistance
Primers, Impregnations & Stains for decorative Wood Coatings
Waterborne Dispersions (LagacyDSM)
Uradil™: Alkyd emulsion
NeoCryl®: Acrylic / Alkyd
NeoCryl®: CationicAcrylic Emulsion
NeoCryl®: SXL AcrylicEmulsion
NeoPac™: Alkyd / PU mod.
XK
89
AZ
516
XK
350
PU
485*
PU
580
excellent impregnation,
good outdoor durability
Anti-knotbleeding,
universal adhesion
controlled erosion,
good reparability
high gloss
more
hydrophobic
Isolation
primers
amine and
VOC free
XK
30
anti bleeding
*: BIT-freeversion
ofNeopacPU-480
HP
1000
Universal primer
with
good adhesion on
numerous
substrates
SP
7450
Universal primers
Interior / exterior
Decovery
grade:
bio-based
Wood and Deck stains
XK
298

11. TABLE -LOGO
11
Primers, Impregnations & Stains for decorative Wood Coatings
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
Decovery
®
SP 7450
Bio-based Acrylic Copolymer
Emulsion
44 < 175 10
Fast drying an& blocking resistance for exterior industrial wood coatings (Joinery). 39%
BiobasedCarbon Content: ASTM D6866-16, Method B
NeoCryl
®
HP 1000 Acrylic Copolymer emulsion 44,5 < 45 < 5
excellent adhesion properties for a broad variety of substrates that are typically very difficult
to stick to, including ceramic tiles, metals; like galvanized steel, aged alkyds, plastics eg..
Very low VOC level to meet
NeoCryl
®
XK-30 Cationic Acrylic Emulsion 42.5 < 100 30
Interior isolation primers, clear and pigmented markers and stains with good stain locking for
nicotine.
NeoCryl
®
XK-89 Polyacrylic alkyd hybrid emulsion45 60 < 4
Controlled erosion and low grain raising,good repairabilityand wet adhesion. For wood and
deck stains.
NeoCryl
®
XK-237
Anionic polyacrylic emulsion,
self crosslinking
44 < 200 8 Very low water uptake, excellent early water resistance also in satin systems.
NeoCryl
®
XK-298
Anionic polyacrylic emulsion,
self crosslinking
44 25 -175 7
Excellent elasticity, good blocking and early water resistance, good wet adhesion, non-
yellowing, low water absorption, good transparency
NeoCryl
®
XK-350 Cationic Acrylic Emulsion 42,5 < 150 36
Stain blocking and knot bleeding resistant clear and pigmented isolation primers. Contains
10% IPA.
NeoPac™PU-485
Alkyd dispersion modified with
aliphatic polyurethane
41-43100 -500 (at 23C) -
Decorative and joinery stains, trim paints, primers and topcoats for interior and exterior on
wood and metal. High hydrophobicity. BIT-free version of PU-480
NeoPac™PU-580
Alkyd dispersion modified with
aliphatic polyurethane
41-43100 -500 (at 23C) -
Decorative and joinery stains, trim paints, primers and topcoats for interior and exterior on
wood and metal. High hydrophobicity. Amine and VOC free.
Uradil™AZ 516
Long oil emulsion based on
tall oil fatty acids
60 150 -450 - Penetration,substrate wetting, adhesion and outdoor durability. For wood and deck stains.

12. PRODUCT MAP SHORT_LOGO
12
Open Time
Gloss
Decorative1K Topcoats for Wood
Waterborne Dispersions (LagacyDSM)
Uradil™: Alkyd emulsion
NeoCryl®: SXL AcrylicEmulsion
NeoPac™: Alkyd / PU mod.
PU
485*
AZ
765
PU
580
E
128
faster drying
lower costs
non yellowing
amine
and VOC
free
chemical &
mechanical
resistance
NeoPac™: PU/Acrylic Dispersion
NeoCryl®: Acrylic Emulsion
XK
188
high gloss
XK
190
XK
237
breathable
low water
absorption
adhesion to
different
substrates
*: BIT-freeversion
ofNeopacPU-480
improved
mechanical
properties
A
820
Wall Paints
SP
7450
Decovery
grade:
bio-based
XK
298

13. TABLE -LOGO
13
Decorative1K Topcoats for Wood
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
Decovery
®
SP 7450Bio-based Acrylic Copolymer Emulsion44 < 175 10
Fast drying an& blocking resistance for exterior industrial wood coatings (Joinery). 39%
BiobasedCarbon Content: ASTM D6866-16
NeoCryl
®
A-820 Anionic acrylic copolymer emulsion 44 < 400 -5
Pigmentatedwall paints, trim paint, deck & fence stains, interior and exterior usage. Good
scrub & stain resistance, durability & adhesion. Compliantto Ecolabel, Nordic Swan, Der
Blaue Engel andAgBB
NeoCryl
®
XK-188 Styrene polyacrylic emulsion 44,5 < 400 6
High gloss, good water resistance, good wet adhesion to wood and old paints, low water
vapourpermeability
NeoCryl
®
XK-190 Anionic acrylic copolymer emulsion 45 < 250 < 0
Tough (hard and flexible),outdoor durable, high block resistance& gloss,good wet adhesion
to many substrates (incl. aged alkyds);alcohol and water resistant
NeoCryl
®
XK-237
Anionic polyacrylic emulsion, self
crosslinking
44 < 200 8 Very low water uptake, excellent early water resistance also in satin systems.
NeoCryl
®
XK-298
Anionic polyacrylic emulsion, self
crosslinking
44 25 -175 7
Excellent elasticity, good blocking and early water resistance, good wet adhesion, non-
yellowing, low water absorption, good transparency
NeoPac™PU-485
Alkyd dispersion modified with
aliphatic polyurethane
41-43
100 -500
(at 23C)
-
Decorative and joinery coatings, stains & trim paints for interior & exterior for wood and metal.
High gloss & hardness, good chemical and mechanical properties. BIT-free version of PU-480
NeoPac™PU-580
Alkyd dispersion modified with
aliphatic polyurethane
41-43
100 -500
(at 23C)
-
Decorative and joinery stains, trim paints, primers and topcoats for interior and exterior on
wood and metal. High hydrophobicity. Amine & VOC free.
NeoPac™E-128
Fatty acid modified polyurethane poly-
acrylic hybrid dispersion
36-38
< 200
(at 25°C)
5
Decorative paints and wood stains with long open time (close to solvent based), excellent
mechanical properties and good outdoor durability.
Uradil™AZ-765
Medium oil alkyd emulsion based on
soybean fatty acids of ~40 % oil length
52-54100 -1000 -
Interior / exterior primers and topcoats for wood, metals and walls with good corrosion-and
yellowing resistance, levelling, gloss, open time and adhesion to different substrates.

14. PRODUCT MAP SHORT_LOGO
14
Blocking resistance
Sandability
Primers for Wood –Industrial Applications
Waterborne Dispersions (LagacyDSM)
NeoCryl®: SXL AcrylicEmulsion
NeoCryl®: Acrylic Emulsion
XK
15
Uradil™: Alkydemulsion
NeoCryl®: Cationic Acrylic Emulsion
AZ
543
XK
350
XK
170
anti knot bleeding,
universal adhesion
Furniture
interior
more
hydrophobic
XK
30
universal
adhesion
XK
298
exterior
flexible
A
639
NeoCryl
®
Alkali Soluble Grades
XK
36
anti bleeding
properties
best wood
penetration
warm wood
coloration
Anti bleeding
Isolation primers
*: BIT-freeversion
ofNeopacPU-480
XK
709
fastest
drying
economical
& hard

15. TABLE -LOGO
15
Primers for Wood –Industrial Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
NeoCryl
®
XK-15
Anionic polyacrylic
emulsion, self crosslinking
45 75 31
Outstanding wood wetting properties, good water and alcohol resistance, high transparency and
good hand crème resistance.
NeoCryl
®
XK-30 Cationic Acrylic Emulsion 42.5 < 100 30
Interior isolation primers, clear and pigmented markers and stains with good stain locking for
nicotine.
NeoCryl
®
XK-36
Alkali Soluble acrylic
copolymer emulsion
40 10 -85 17
Semi hardbuttough films, stain and bleeding resistant when properly
pigmented/formulated, applicable by roller coating techniques
NeoCryl
®
XK-170
Anionic styrene acrylic
copolymer emulsion
45 200 –500 33
Hard and good outdoor durability, high gloss and resistant to blocking,
goodwet adhesion to many substrates including fresh and aged alkyd-based coatings and stoving
enamels, good water and humidity resistance
NeoCryl
®
XK-298
Anionic polyacrylic
emulsion, self crosslinking
44 25 -175 7
Excellent elasticity, good blocking and early water resistance, good wet adhesion, non-yellowing,
low water absorption, good transparency
NeoCryl
®
XK-350 Cationic Acrylic Emulsion 42,5 < 150 36
Stain blocking and knot bleeding resistant clear and pigmented isolation primers. Contains 10%
IPA.
NeoCryl
®
XK-639
Styrene acrylic
copolymer emulsion
45 230 67 Economical general-purpose resin with high hardnessand goodblocking resistance.
NeoCryl
®
XK-709
anionic, modified acrylic
copolymer emulsion
42.5 < 200 33
Universal, easy to formulate acrylic emulsion for fast drying interior and exterior industrial wood
coatings with excellent sandability
Uradil™AZ-543
Water soluble modified
linseed oil alkyd
100 600 -800 - Wood impregnation with excellent wood penetration and wetting properties.

16. PRODUCT MAP SHORT_LOGO
16
Water resistance
Blocking resistance
1K Topcoats for Wood –Industrial Exterior (Joinery) Applications
Waterborne Dispersions (LagacyDSM)
NeoCryl®: SXL AcrylicEmulsion
NeoRez®: PU-Dispersion
*R
1007
NeoCryl®: Acrylic Emulsion
*R
2005
*XK
99
XK
237
XK
232
more
hydrophobic
lower VOC
demand
lower
water
uptake
Improved
scratch
resistance
* usedasblendpartner
highest
elasticity
XK
231
XK
190
R
3961
PVC
adhesion
higher
flexibility
better early
blocking resistance
SP
7450
Decovery grade:
bio-based
PeelableCoatings
XK
298

17. TABLE -LOGO
17
1K Topcoats for Wood –Industrial Exterior (Joinery) Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
Decovery
®
SP 7450
Bio-based Acrylic Copolymer
Emulsion
44 < 175 10
Fast drying an& blocking resistance for exterior industrial wood coatings (Joinery). 39% bio-based
carbon content: ASTM D6866-16, Method B
NeoCryl
®
XK-99 Anionic polyacrylic emulsion 44 < 150 4
Excellent water resistant and good blocking and alkali resistant. Suitable for clears and opaque
coatings.
NeoCryl
®
XK-190
Anionic acrylic copolymer
emulsion
45 < 250 < 0
Tough (hard and flexible),outdoor durable, high block resistance& gloss,good wet adhesion to many
substrates (incl. aged alkyds);alcohol and water resistant
NeoCryl
®
XK-231
Anionic polyacrylic emulsion, self
crosslinking
42 < 150 20Good blocking properties, non yellowing, good adhesion on PVC, good transparency
NeoCryl
®
XK-232
Styrene acrylic copolymer
emulsion, selfcrosslinking
45 40 66Very hydrophobic,self crosslinking emulsionwith good early blocking resistance at high film thickness.
NeoCryl
®
XK-237
Anionic polyacrylic emulsion, self
crosslinking
44 < 200 8Very low water uptake, excellent early water resistance also in satin systems.
NeoCryl
®
XK-298
Anionic polyacrylic emulsion, self
crosslinking
44 25 -175 7
Excellent elasticity, good blocking and early water resistance, good wet adhesion, non-yellowing, low
water absorption, good transparency
NeoRez
®
R-1007
Solvent free PU Dispersion,
soft & very flexible
40 120 <0
UV resistant, flexibilizingresin (elongation 650 %) for acrylic emulsions in wood & cork parquet
lacquers & as single binder for very flexible substrates. Polymeric film forming agent in acrylic lacquers.
NeoRez
®
R-2005
Solvent free PU Dispersion, free
of plasticizers, heavy metals/TEA
35 350 <0
Hard but flexible (elongation 160%) binder for wood and parquet lacquers. Also suitable for wear
resistant floor polishes. Can be used as single binder or in combination with polyacrylic emulsions for 1
& 2 pack systems
NeoRez
®
R-3961 Anionic Aliphatic PU Dispersion31 10 -400
Hard, flexible, chemical &abrasion resistant;Elongation 270%, Könighardness 130“; good water,
humidity & UV-resistance,good adhesion to plastics (e.g.PVC, ABS,PC)& metal.

18. PRODUCT MAP SHORT_LOGO
18
Stain / Chemical resistance
Blocking resistance
1K Topcoats for Wood –Industrial Interior (Furniture) Applications
Waterborne Dispersions (LagacyDSM)
NeoPac™: PU/AcrylicDispersion
NeoCryl®: SXL AcrylicEmulsion
NeoCryl®: Acrylic Emulsion
NeoRez™: PU fattyacidmod.
A
639
XK
205
XK
14
XK
12
XK
16
E 225
E 160
*E 129
R
9029
better stain
resistance
improved wood
wetting, abrasion
& scratch resistance
higher
transparency
better scratch
resistant
higher
hardness
* usedasblendpartner
cost
effective
SP
7000
Decovery
grade:
bio-based
better mechanical
properties

19. TABLE -LOGO
19
1K Topcoats for Wood –Industrial Interior (Furniture) Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
Decovery
®
SP 7000
Biobasedurethane acrylic
copolymer dispersion
39 < 400 67
Industrial interior wood,plastic & concrete floor coatings;good wood wetting and flow,
chemical,solvent,hand cream resistance,21% bio-based content
NeoCryl
®
XK-12
Anionic polyacrylic emulsion, self
crosslinking
45 75 29 Good resistanceto water, alcohol and chemicals. Hot blocking resistance.
NeoCryl
®
XK-14
Anionic polyacrylic emulsion, self
crosslinking
40 50 33
Good resistance to water and alcohol and chemicals, good wood wetting and high
transparency,low foaming tendency and good flow and levelling.
NeoCryl
®
XK-16
Anionic polyacrylic
emulsion, self crosslinking
40 50 34 High hardness and good blocking resistant,good resistant to water and alcohol.
NeoCryl
®
XK-205
Styrene acrylic
copolymer emulsion
42 10 -100 55 General purpose resin with good hardness and good wood wetting properties.
NeoCryl
®
A-639
Styrene acrylic
copolymer emulsion
45 230 67 Economical general-purpose resin with high hardnessand goodblocking resistance.
NeoPac™E-125
Aliphatic,self crosslinking urethane
acrylic copolymer dispersion
35 < 10Good scratch resistance and chemical resistance
NeoPac™E-129
Polyurethane polyacrylic copolymer
dispersion
40 < 200 60
Transparent and pigmented industrial wood -, plastic -. and concrete coatings with good tire
resistance, hardness, wood wetting and levelling. Furthermoregood blocking, chemical and
excellent imprint resistance.
NeoPac™E-160
Polyurethane polyacrylic copolymer
dispersion
34 29 Excellent stain and coffee resistance in white pigmentedcoatings
NeoRez® R-9029
Plasticizer free, fatty acid modified
aliphatic polyurethane dispersion
32 160 <0
Good wood wettingand high abrasion & scratch resistance.
Alternative to solvent basedurethane alkyds.

20. PRODUCT MAP SHORT_LOGO
20
Wood coloration
Sand ability
Primers for Wood -Flooring Applications
Waterborne Dispersions (LagacyDSM)
NeoCryl®: CationicAcrylic Emulsion
NeoCryl®: SXL AcrylicEmulsion
XK
12
NeoCryl®: Acrylic Emulsion
XK
30
XK
68
General primers
Isolation
primers
warm reddish
wood coloration

21. TABLE -LOGO
21
Primers for Wood -Flooring Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
NeoCryl
®
XK-12
Self crosslinking Acrylic
copolymer emulsion
45 75 29
Water, chemical,alcohol resistant. Very block resistant.
Neutral wood coloration and fast drying. Good sand ability.
NeoCryl
®
XK-30 Cationic Acrylic Emulsion 42.5 < 100 30
Interior isolation primers, clear and pigmented markers and stains
with good stain locking fornicotine.
NeoCryl
®
XK-68 Acrylic copolymer emulsion 47.5 300 35
Warm woodcoloration due to low pH character (reddish tone).
Good drying and sand ability.

22. PRODUCT MAP SHORT_LOGO
22
Stain resistance
Drying speed
for waterborne 1K Parquet Lacquers
Waterborne Dispersions (LagacyDSM)
Crosslinkers:
NeoAdd
PAX
523
NeoPac™: PU/AcrylicDispersion
NeoCryl®: SXL AcrylicEmulsion
*XK
12
NeoRez®: PU-Dispersion
NeoRez™: PU fattyacidmod.
*R
2005
R
2190
faster drying
& lower costs
hard but
flexible
R
9029
higher scratch
resistance
improved indoor air
quality (lower co-solvent
demand)
Solvent-borne look and feel,
more body, higher gloss
* usedasblendpartner
XK
14
E
180
E
108
good wood wetting
& transparency
good wood
coloration
solvent-
free
SP
2022
Decovery grade:
bio-based
deep matt
R
2180

23. TABLE -LOGO
23
for waterborne 1K Parquet Lacquers
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
Decovery
®
SP 2022
Bio-based Aliphatic self-crosslinking
Poly Urethane dispersion
35 100 -4 00
Self-matting bio-based solution for seamless & wood floors,non-yellowing, neutral wood
coloration, Excellent chemical, BHMR,scuff & wear resistance. 32% Bio-based content
NeoCryl
®
XK-12
Modifiedanionic polyacrylic
emulsion, self crosslinking
45 75 29
Neutral appearance, good chemical resistance and wetting properties. Ideal economical
combination partner for NeoRez R-2180and R-2190.
NeoCryl
®
XK-14
Anionic polyacrylic emulsion, self
crosslinking
40 50 33
Good resistance to water and alcohol and chemicals, good wood wetting and high transparency,
low foaming tendency and good flow and levelling.
NeoRez
®
R-2005
Solvent free PUD, free of
plasticizers, heavy metals and TEA
35 350 <0
Hard but flexible (elongation 160%) binder for wood and parquet lacquers. Also suitable for wear
resistant floor polishes. Can be used as single binder or in combination with polyacrylic emulsions
for 1 & 2 pack systems
NeoRez
®
R-2180
Solvent-free aliphatic polyurethane
dispersion for low VOC formulations
35 50 <0
High end 1K and 2K parquet and cork lacquers with good yellowing-, chemical-, abrasion-&
scratch resistance , good levelling and optimal hardness/ toughness balance,. Complies with Gis
code W2 (Germany).
NeoRez
®
R-2190
Aliphatic self crosslinking
polyurethane dispersion
37-39 25 -150 <0
Very low VOC, high end 1K & 2K parquet lacquers with good yellowing-, chemical-, abrasion-&
scratch resistance and good levelling. Complies with indoor air quality legislations like AgBB.
NeoRez
®
R-9029
Plasticizer free, fatty acid modified
aliphatic polyurethane dispersion
32 160 <0
For 1 pack parquet lacquers withgood wood wetting, solvent borne lookand high scratch and
Black Heel mar resistance. Alternative to solvent basedurethane alkyds.
NeoPac™R-9045
Modified aliphatic polyurethane
polyacrylic hybrid dispersion
45 250 <0
Higher solidsbinder with good scratch and abrasion resistance,excellent clarity, recoatability and
sandability. To reach high chemicalresistance level addition of a curing agent e.g.Cross linker
CX-100 is recommended.
NeoPac™E-108
Aromatic polyurethane polyacrylic
hybrid dispersion
33 10 -60 < 4
Tough (hard and flexible) and clear, high water and ethanol resistance, low level of thermo-
plasticity, goodchemical & abrasion resistance, easy to apply, good flow out
NeoPac™E-180
Aromatic polyurethane polyacrylic
hybrid dispersion
33 25 -200 19
Easy to apply, good flow out, tough (hard and flexible) and clear films, excellent chemical
resistance, low level of thermo-plasticity, excellent abrasion & scratch resistance

24. PRODUCT MAP SHORT_LOGO
AZ
760
24
Corrosion resistance
Humidity resistance
1K Primers for Metal Applications
Waterborne Dispersions (LagacyDSM)
NeoCryl®: AcrylicEmulsion
Uradil™: Alkydemulsion
Haloflex™: CationicVinyl-Dispersion
XK
82
XK
205
XK
85
XK
87
H
202
outstanding
salt spray
& humidity
resistance
+ high solids
harder + more
cost effective
Clear
coats
better
sandability
High solids,
simple
formulations
AZ
765
good blocking
and hardness
xylene-free

25. TABLE -LOGO
25
1K Primers for Metal Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
NeoCryl
®
XK-82
Styrene acrylic
copolymer emulsion
40 60 44
Standard polyacrylic emulsion for waterborne primerswith good hardness,humidity and
corrosion resistance.
NeoCryl
®
XK-85
Styrene acrylic
copolymer emulsion
40 150 19
For waterborne primers with good overcoatability, corrosion and humidity resistance.
Excellent performance as metal clear coat. Alsofor temporary protection.
NeoCryl
®
XK-87
Styrene acrylic
copolymer emulsion
51 250 27
High solidsemulsion for waterborne primers with excellent dry and wet adhesion to
various metals, corrosion and humidity resistance.
NeoCryl
®
XK-205
Styrene acrylic
copolymer emulsion
42 10 -100 55
General purpose acrylic emulsionwithfast drying, good hardness, yellowing resistance
and compatibility with otherbinders.
Uradil™AZ-760
Medium oil alkyd emulsion based on soybean
fatty acids with approx. 40 % oil length
53
100 -1000
(at 23°C)
-
Waterborne primers, single layer and topcoats with solvent basedbehavior like leveling
and drying speed.Very high gloss, good hardness, blocking resistance, durability &
water resistance.
Uradil™AZ-765
Medium oil alkyd emulsion based on soybean
fatty acids with approx. 40 % oil length
53 100 -500 - Xylene-free version of AZ 760
Haloflex™202
Cationic polyvinyl polyacrylic copolymer
emulsion
60 50 12
Very good barrier propertiesto water, water vapor, oxygen, carbon dioxide and radon
and thus outstanding corrosion and humidity resistance. Well suitable for primers as well
as indoor single layer clear or pigmented spray and dip coatings .

26. PRODUCT MAP SHORT_LOGO
26
Drying speed
Hardness
1K Topcoats for Metal Applications
Waterborne Dispersions (LagacyDSM)
AZ
760
NeoCryl®: AcrylicEmulsion
NeoCryl®: SXL AcrylicEmulsionNeoPac™: Alkyd/ PU mod.
Uradil™: Alkydemulsion
PU
485
XK
12
XK
205
good early
water
resistanceHigh gloss &
good resistance
faster drying
& no yellowing
very broad
compatibility
higher
gloss
AZ
765
Xylene free
*: BIT-freeversion
ofNeopacPU-480

27. TABLE -LOGO
27
1K Top Coatsfor Metal Applications
Waterborne Dispersions (LagacyDSM)
Resin Resin Type
Solids
[%]
Viscosity
[mPas@25°C]
MFT
[°C]
Specific areas &key performance
NeoCryl
®
XK-12
Modifiedanionic polyacrylic
emulsion, self crosslinking
45 75 29
Fast drying emulsionwith good early water, chemical and blocking
resistance for primers and topcoats.Good gloss, outdoor and scratch
and yellowing resistance in QUVtests.
NeoCryl
®
XK-205
Styrene acrylic
copolymer emulsion
42 10 -100 55
General purpose acrylic emulsionwithfast drying, good hardness,
yellowing resistance and compatibility with otherbinders.
NeoPac™PU-485
Alkyd dispersion modified
with aliphatic polyurethane
41-43 100-500 -
Fast drying primers,single layer and topcoats with good leveling, high
hardness and gloss,good gloss retentionand water resistance.
BIT-free version of PU-480
Uradil™AZ-760
Medium oil alkyd emulsion
based on soybean fatty acids
with approx. 40 % oil length
53
100 -1000
(at 23°C)
-
Waterborne primers, single layer and topcoats with solvent based
behavior like levelingand drying speed.Very high gloss, good
hardness, blocking resistance, durability & water resistance.
Uradil™AZ-765
Xylene-free Medium oil alkyd
emulsion based on soybean
fatty acids with approx. 40 %
oil length
53
100 –500
(at 23°C)
-
Goodleveling&drying speed, high gloss level&film hardness, good
blocking, yellowing & water resistance, Exterior durability

28. TEXT -LOGO
Covestro CA products for various Coating Technologies
28
1K
2K
Moisture Curing 1K PUR systems
DesmodurE+ Humidity
Solventborne& -free 2K PUR systems
Desmophen+ Desmodur
Waterborne 1K systems
Neocryl, NeoRez& NeoPac
Waterborne 2K PUR systems
Bayhydrol+ Bayhydur

29. PRODUCT MAP SHORT_LOGO
ultra
2759
quix
306-70
ultra
2487/1
ultra
3100
ultra
2655
29
Chemical resistance
Easy Mixing
Bayhydur
®
grades for waterborne 2K PUR Parquet Lacquers
Hydrophilic Polyisocyanates
ultra
305
ultra
2700
Ultra
2858
ready
to use
faster drying &
easy mixing
ready
to use
longer potlife
high gloss with
hand mixing better stain resistance
faster drying &
longer potlife
faster physical
drying
uHDI grades uTDI/HDI gradesuIPDI grades
ultra
401-70
in combination
with HDI grades

30. TEXT -LOGO
Aliphatic hydrophilic Polyisocyanates
30
Bayhydur
®
& Bayhydurultra for waterborne 2K PUR systems
Bayhydur
®
Monomer base Type Solid content[%]
Viscosity@ 23°C
[mPas]
NCO-content [%] on
supplyform
Functionality
ultra 3100 HDI
polyether-
modified
1st generation
100 2800 17.4 3.1
XP 2451/1 HDI 100 800 20.3 3.0
ultra 401-70 MPA IPDI 70 in MPA 1500 9.4 2.9
ultra 401-70 MPA/X IPDI 70 in MPA/X 600 9.4 2.9
ultra 304 HDI
polyether
modified2nd
generation
100 4000 18.2 3.8
ultra 305 HDI 100 6500 16.2 4.0
ultra 2700 HDI 65 in DPGDME 75 10.6 4.0
ultra 2487/1 HDI
ionically
modified
3rd generation
100 5400 20.6 3.4
2547 HDI 100 650 22.5 3.0
ultra 2655 HDI 100 3500 20.8 3.2
ultra 2759 IPDI 70 in MPA 6000 11.0 3.2
ultra 2858 HDI/IPDI 70 in PGDA 500 13.3 3.4
CQ ultra 701-90 PDI 90 in PGDA 5000 17.9 3.6
quix306-70 HDI/TDI 70 in MPA 250 13.5 3.3

31. PRODUCT MAP SHORT_LOGO
31
Drying Speed
Chemical Resistance
Bayhydrol
®
U & A for waterborne 2K PUR industrial Wood & Furniture Coatings
Polyurethane and Polyacrylic Polyol Dispersions
U
2755/1
A
2695
A
2470
A
2770
A
2651
A
242
U
2757
Natural touch
only in combination
A
2427
lower solvent content
& faster drying speed
highest chemical
resistance
Anti-Knot
bleeding
Primers
Multi purpose
Wood coatings
improved
mechanical
properties
Solvent-based look
Matt &
semi gloss
pigmented
coatings
APolyacrylic Secondary Dispersions
APolyacrylic Primary Dispersions
uPolyurethane Dispersions
A
2846
1K & 2K systems

32. TABLE -LOGO
32
BayhydrolSolid
content [%]
OH content on
solids [%]
Neutralizing
agent
Organic Co-
solvent [%]
Properties/Applications
A 242 42 4.0 NH
3 none
Good chemical resistance; near zero VOC formulations;
anti-knot-bleeding primers
A 2427 42 2.0 NH
3 none
Very fast drying; 1K & 2K near zero VOC formulations, matt & semi gloss
pigmented primers, fillers & top coats
A 2470 45 3.9
DMEA/
Triethanolamine
4 SN + 4 PnB
High performance clear & top coots with excellent gloss, chemical &
weather resistance
A 2651 41 3.0
DMEA/
Triethanolamine
3.4 PnB
Fast drying clear formulations with solvent-like wood grain accentuation and
good chemical & stain resistance
A 2695 41 5.0
DMEA/
Triethanolamine
7.2 PnB
Clear & top coats with hardness, good outdoor resistance and highest
chemical & stain resistance (e.g. against graffiti cleaners)
A 2770 44 3.9 DMEA 3.6 PnB Low VOC alternative to A 2470 with faster drying speed
A 2846 40 1.5 NH
3 none
Self-crosslinking acrylic emulsion with fast drying, good chemical resistance
& hardness as 2K PUR and as 1K formulations
U 2755/1 35 3.0 DMEA none
Very fast drying clear formulations with very good wood grain accentuation,
high hardness & stain resistance and near zero VOC
U 2757 52 1.8 DMEA none
In combination with e.g. A 2651 for natural wood touch formulations with
good hydrolysis resistance, long potlifeand near zero VOC
Bayhydrol
®
U & A for waterborne 2K PUR industrial Wood & Furniture Coatings
Polyurethane and Polyacrylic Polyol Dispersions
SN: Solvent naphta DMEA: Dimethylethanolamine TEtA: Trriethanolamine

33. DISCLAIMER
33
Disclaimer
The content in this presentation is provided to you by IMCD N.V (“IMCD”) and intended for your personal
informationonly. All information appearing herein is based on our present knowledge and experience (“as is”) and
IMCD makesno representations as to its accuracy or sufficiency. To the extent information from third parties is used
for or includedin this presentation, we have not executed an independent verification and expressly do not represent,
warrant,undertake or guarantee that the content herein or underlying information is, at any time, correct, accurate,
complete,non-misleading or fit for any purpose or use.
This presentation does not provide any form of (commercial, investment or financial service) advice, nor does
itcontain recommendations regarding any decision, and should not be treated as such.
This presentation is considered confidential and any disclosing, distribution, copying or dissemination of
thispresentation or parts thereof,
without the expressed prior consent of IMCD strictly prohibited.