Plastic moulding methods

PLASTIC MOULDING PROCESS:
1. Compression Moulding.
2. Transfer Moulding.
3. Injection Moulding.
4. Extrusion Moulding
5. Calendering
6. Laminating

1. PLASTIC MOULDING
METHODS
ME 405 -UNIT 111ME 405 -UNIT 111

2. 
Mouldingof plastics comprises forming an
article to the desired shape by application
of heat and pressure to the moulding
compound in a suitable mould and compound in a suitable mould and
hardening the material in the mould.

There are two types of material generally
used : 1.Thermosetting Plastic
2. Thermo Plastic

3. 
COMPRESSION MOULDING

TRANSFER MOULDING

TRANSFER MOULDING

INJECTION MOULDING

EXTRUSION MOULDING

4. 
THERMOSETTING material are generally
processed by Compression Moulding
and Transfer Moulding.

THERMOPLASTIC material are generally
processed by Injection mouldingand
Extrusion Moulding.

5. 
In COMPRESSION
mouldingprocess
the monomers are
partially
polymerisedin a polymerisedin a
separate operation
and the
polymerisation
reaction
completes in a
mould.

6. 
Partially polymerized material is prepared as
pallets for COMPRESSION moulding.

It is placed in heated mould.

After the compound is softened and becomes
plastic, the upper part of the die moves
downwards, compressing the materials to the
plastic, the upper part of the die moves
downwards, compressing the materials to the
required shape and density.

Continuous heat and pressure produce the
chemical reaction, leading to cross linking
between the molecule chains, that hardens the
thermosetting material.

The mould remains closed until the curing is
complete.

7. 
COMPRESSION mouldingis suitable for
large, bulk parts of both Thermosetting and
Thermoplastic materials.

COMPRESSION mouldingis also suitable for

COMPRESSION mouldingis also suitable for
making small parts of Thermosetting
materials.

Mouldinglarge size parts by
COMPRESSION mouldingmight be a
problem.

8. 
The mouldingTemperature of
thermosetting materials ranges from 150°C
to 180°C.

The mouldingPressure ranges from 135 -

The mouldingPressure ranges from 135 -
535 kgf/cm².

The Time required to harden the mould
piece ranges from 1 to 15 minutes
depending upon the maximum thickness
of the mouldedarticle and the cooling
facilities of the die.

9. 
TRANSFER mouldingcan be generally employed for
mouldingthick sections.

In TRANSFER mouldingprocess, charge of moulding
powder is forced from a cylinder through a relatively
restricted opening into the main mould.restricted opening into the main mould.

Due to flow through restricted passage, the moulding
powder becomes heated much more rapidly and
uniformly.

A high pressure in the order of 700 kg/cm² is
applied.

Ejector pins are provided at suitable sections in
order to facilitate the removal of product from the
mould.

10. 
In TRANSFER moulding, the THERMOSETTING
mouldingpowder is prepared by mixing filler with
resin which is only partly condensed and makes it
capable of being softened on re-heating.

The resin and the filler is mixed together and heated
until the desired characteristics of the moulding
poederis attained. The most commonly used fillers
are wood, flour, nylon and glass.

12. In TRANSFER moulding, the following points are to
be kept in mind:

Material should flow easily in the mould to take the
required shape.

All parts of the charge must be heated so as to

All parts of the charge must be heated so as to
harden

When the sections are thick, it become necessary to
pre-heat the charge of material before placing it in
mould.

Usually ejector pins are provided at suitable sections
in order to facilitate the removal of product from the
mould.

14. 
InINJECTIONmouldingprocessthegranularmoulding
materialisloadedintoahopperfromwhereitis
meteredoutbyaheatingcylinderbyafeedingdevice.

Theexactamountofmaterialisdeliveredtothe
materialwhichisrequiredtomeltcompletely.
Theinjectionrampushesthematerialintotheheating

Theinjectionrampushesthematerialintotheheating
cylinderandindoingsopushesasmallamountof
heatedmaterialoutoftheotherendofthecylinder
throughthenozzleandscrewbushingandintothe
cavitiesoftheclosedmould.

Thematerialiscooledtoarigidstateinthemould.

Themouldisthenopenedandthepieceisejectedout.

16. 
The temperature to which the
material is raised in Injection
mouldingin the heating cylinder
is usually between 180 -280°C.

Thehigherthetemperaturethe
lowertheviscocityandmorelowertheviscocityandmore
readilyitcanbepushedintothe
die.

INJECTIONmouldingprocess
makesuseofheatingsoftening
characteristicsofThermosetting
plastics.

These material soften when
heated and hardens when cools.

18. 
EXTRUSION mouldingprocess is a continuous operation in
which powdered polymer or monomer is fed by a screw
along a cylindrical chamber.

As the powder moves towards the die, it is heated and melts.

The molten plastic is forced through a die opening of

The molten plastic is forced through a die opening of
desired shape.

The material in granular form together with necessary
additives is placed into a feed hopper which feeds the
cylinder of the extruding machine.

A rotating screw is used for carrying and mixing of material
through cylinder and forcing it through a die of required
shape.

20. 
The BLOW mouldingprocess is applied
to only thermoplastics which are used for
producing hollow objects such as bottle
by applying air pressure.by applying air pressure.

The air under pressure is blown into the
tube, which causes the tube to expand to
the walls of cavity.

22. 
Sheets of PVC can be produced by
CALENDERING process.

The polymer is first mixed with the
plasticizers and other additives such
as colouringagents. The mix is then
heated for a short time to produce a heated for a short time to produce a
rough sheet which is fed through a
series of roll.

The thickness is gradually reduced,
and at the same time a smooth
textured surface is produced.

The finished thickness is
determined by setting the thickness
between the paired of rolls.

24. 
Laminating plastics comprise sheets
of paper, fabric asbestors, wood or
similar materials, which are first
coated with resin and bonded
together by heat and pressure to
form commercial materials.form commercial materials.

These material are hard, strong,
impact resisting, unaffected by heat
or water and having good machining
characteristics.

Commercially laminates are
available in sheets, rods, tubes.
Among which sheet form is common.